CM353, Highest molecular weight, relatively narrow molecular weight distribution, highest Mooney viscosity and best physical performance. It is equivalent to Tyrin CM0836 & Tyrin CM3551 from Dow Chemical . 

Tech Specs: 

Items                                                                            UNIT                                               INDEX                                              Test Method 

Chlorine content                                                            %                                                  35±1                                                    ISO 7725 

Heat of Fusion                                                               J/g                                                 ≤2.0                                                         DSC 

Volatile Matter component                                          %                                                  ≤0.4                                                      ISO 1269 

Rate of filtration(40 mesh)                                            %                                                 ≥98                                                            -- 

Shore Hardness A                                                            °                                                   ≤56                                                      ISO 7619 

Tensile strength                                                             Mpa                                               ≥8.0                                                        ISO 37 

Elongation at break                                                         %                                                 ≥800                                                       ISO 37

Mooney Viscosity ML(121°C 1＋4)                              --                                                 85-100                                                         -- 

Whiteness E457                                                               °                                                    ≥80                                                             --

Application: High viscosity grade for highly filled hose, cable jackets, HPN cords, sponge and molded Products.Not only it can be used as halide rubber solely but also it can be mixed with CR, CSM, NBR, SBR and NR at any proportion.

Package : 25kg PP valve bag ; 25kg Woven bag with PE liner ; 500/550kg super sack The product can be stored under appropriate conditions for two years. But please keep products store in a dry ventilated environment (temperature should not exceed 30°C, in low humidity). Inappropriate storage environment may cause agglomeration.Especially at high temperatures & high humidity, it is recommended not to stack more than 30 days long, it may increase agglomeration phenomenon. Agglomeration does not affect the quality and performance , not a quality problem, but Agglomeration material is smashed before using . It is not dangerous cargo .You should handle the material according to the instruction described on MSDS.The MSDS is available from sales department once required.